Ottone - JIS H 2202:2016

LegaCuPbSnFeAlNiMnSbPSiZnSAsBiCdCrMgCoSe
CACIN201 min
max
 83 - - - - - - - - - 10 - - - - - - - -
88 0.5 0.1 0.2 0.2 0.2 - - - - 20 - - - - - - - -
Ricerche correlate:
CAC201
CACIN202 min
max
 65 0.5 - - - - - - - - 20 - - - - - - - -
70 3 1 0.6 0.5 1 - - - - 40 - - - - - - - -
Ricerche correlate:
CAC202
CACIN203 min
max
 58 0.5 - - - - - - - - 20 - - - - - - - -
64 3 1 0.6 0.5 1 - - - - 50 - - - - - - - -
Ricerche correlate:
CAC203
CACIN211 min
max
 65.5 0.1 1.1 - 0.01 - - 0.06 0.05 - 20 - - - - - - - -
68.5 2 1.5 0.2 0.1 0.2 - 0.15 0.1 0.05 40 - - - - - - - -
Ricerche correlate:
CAC211, CAC211C

Ottone - ASTM B30-23

LegaCuPbSnFeAlNiMnSbPSiZnSAsBiCdCrMgCoSe
C85200
(B, E, A)
min
max
 70 1.5 0.8 - - - - - - - 21 - - - - - - - -
73 3.5 1.7 0.5 0.005 0.8 - 0.2 0.01 0.05 27 0.05 - - - - - - -
Ricerche correlate:
ASTMC85200, CDA85200
C85400
(B, F, A)
min
max
 66 1.5 0.5 - - - - - - - 25 - - - - - - - -
69 3.5 1.5 0.5 0.005 0.8 - - - 0.05 31 - - - - - - - -
Ricerche correlate:
ASTMC85400, CDA85400
C85470
(D, A)
min
max
 60 - 1 - 0.1 - - - 0.02 0.4 20 - - - - - - - -
65 0.09 4 0.2 1 - - - 0.25 1 40 - - - - - - - -
Ricerche correlate:
ASTMC85470, CDA85470
C85700
(B, G, A)
min
max
 58 0.8 0.5 - - - - - - - 33 - - - - - - - -
63 1.5 1.5 - 0.8 0.8 - 0.5 - 0.05 40 - - - - - - - -
Ricerche correlate:
ASTMC85700, CDA85700
C85800
(B, G, A)
min
max
 57 - - - - - - - - - 31 - - - - - - - -
- 1.5 1.5 0.5 0.5 0.5 0.25 0.05 0.01 0.25 41 0.05 0.05 - - - - - -
Ricerche correlate:
ASTMC85800, CDA85800

Note

A In questa lega il cobalto è incluso nel conteggio del nickel
B Nel determinare il rame minimo, il rame può essere calcolato come rame più nichel
D Rame+Somma degli elementi nominati, 99.5%
E Rame+Somma degli elementi nominati, 99.1%
F Rame+Somma degli elementi nominati, 98.9%
G Rame+Somma degli elementi nominati, 98.7%

Ottone - UNI EN 1982:2017

LegaCuPbSnFeAlNiMnSbPSiZnSAsBiCdCrMgCoSe
CB750S
(1, 2)
min
max
 63 1 - - - - - - - - 20 - - - - - - - -
66 2.8 1.5 0.7 0.1 1 0.2 - 0.02 0.04 40 - - - - - - - -
Ricerche correlate:
CC750S, CUZN33PB2-B, CUZN33PB2-C, SCB3, GB-CUZN33PB, GBCUZN33PB, GB-MS65A, GBMS65A
CB751S
(2)
min
max
 63.5 0.8 - 0.25 - - - - - 0.7 20 - - - - - - - -
65.5 2 0.8 0.5 0.1 0.8 0.1 0.05 - 1 40 - - - - - - - -
Ricerche correlate:
CC751S, CUZN33PB2SI-B, CUZN33PB2SI-C
CB754S
(2, 15)
min
max
 58 0.5 - - 0.1 - - - - - 20 - - - - - - - -
62 2.4 1 0.7 0.8 1 0.5 - 0.02 0.05 40 - - - - - - - -
Ricerche correlate:
CC754S, CUZN39PB1AL-B, CUZN39PB1AL-C, DCB3, CUZN40PB
CB766S
(2)
min
max
 60 - - - 0.6 - - - - - 20 - - - - - - - -
63 0.4 0.4 0.4 1.8 1.8 0.4 0.05 0.02 0.5 40 - - - - - - - -
Ricerche correlate:
CC766S, CUZN37AL1-B, CUZN37AL1-C
CB767S
(2)
min
max
 59 - - - 0.1 - - - - - 20 - - - - - - - -
64 0.1 0.1 0.4 0.8 0.8 0.4 - 0.05 0.05 40 - - - - - - - -
Ricerche correlate:
CC767S, CUZN38AL-B, CUZN38AL-C
CB770S
(3)
min
max
 61.5 0.2 - - 0.5 - - - - - 30 - 0.04 - - - - - -
63.5 1.6 0.3 0.3 0.7 0.2 0.1 - - - 40 - 0.14 - - - - - -
CB773S
(3)
min
max
 57 - - - 0.1 - - - - - 40 - - - - - - - -
59 0.1 0.3 0.3 0.3 0.02 0.02 0.02 0.02 0.02 50 - - - - - - - -
Ricerche correlate:
CC773S, CUZN42AL-B, CUZN42AL-C

Note

1 Per i lingotti utilizzati in colata in sabbia a tenuta di pressione e in colata in centrifuga, l'alluminio dev'essere 0.02% max
2 Nickel incluso nel conteggio del rame
3 Per applicazioni per acqua potabile, possono essere applicate alcune restrizioni alla composizione chimica di alcuni elementi in accordo con le regole/leggi nazionali
15 Per i lingotti utilizzati in colata in sabbia o in colata in centrifuga, l'alluminio dev'essere 0.02% max