UNI EN 1982:2017
UNI EN 1982:2017 - Aluminium bronze
Notes
2 | Nickel is included in the copper counting |
10 | For castings for sea-water applications, the aluminium content shall be such that Al %< (8.2 + 0.5Ni %) |
11 | For permanent mould castings, the maximum copper content for ingots and castings shall be 88.5% |
12 | For permanent mould castings, the minimum iron content of ingots and castings shall be 3.0% and the minimum nickel content shall be 3.7% |
13 | For permanent mould castings the minimum iron content of ingots and castings shall be 3.0% and the minimum aluminium content shall be 9.0%. In this case, the maximum copper content shall be 84.5% |
UNI EN 1982:2017 - Brass
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>63 | 1 | - | - | - | - | - | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
66 | 2.8 | 1.5 | 0.7 | 0.1 | 1 | 0.2 | - | 0.02 | 0.04 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>63.5 | 0.8 | - | 0.25 | - | - | - | - | - | 0.7 | 20 | - | - | - | - | - | - | - | - | |||
65.5 | 2 | 0.8 | 0.5 | 0.1 | 0.8 | 0.1 | 0.05 | - | 1 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>58 | 0.5 | - | - | 0.1 | - | - | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
62 | 2.4 | 1 | 0.7 | 0.8 | 1 | 0.5 | - | 0.02 | 0.05 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>60 | - | - | - | 0.6 | - | - | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
63 | 0.4 | 0.4 | 0.4 | 1.8 | 1.8 | 0.4 | 0.05 | 0.02 | 0.5 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>59 | - | - | - | 0.1 | - | - | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
64 | 0.1 | 0.1 | 0.4 | 0.8 | 0.8 | 0.4 | - | 0.05 | 0.05 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>61.5 | 0.2 | - | - | 0.5 | - | - | - | - | - | 30 | - | 0.04 | - | - | - | - | - | - | |||
63.5 | 1.6 | 0.3 | 0.3 | 0.7 | 0.2 | 0.1 | - | - | - | 40 | - | 0.14 | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>57 | - | - | - | 0.1 | - | - | - | - | - | 40 | - | - | - | - | - | - | - | - | |||
59 | 0.1 | 0.3 | 0.3 | 0.3 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | 50 | - | - | - | - | - | - | - | - | ||||
Notes
1 | For ingots intended for the manufacture of pressure-tight sand castings and centrifugal castings, aluminium shall be restricted to 0.02% max. |
2 | Nickel is included in the copper counting |
3 | For drinking water applications, restrictions to the chemical composition of some materials listed in this table may apply according to national regulations/laws |
15 | For ingots for the manufacture of sand castings or centrifugal castings, the aluminium content shall be restricted to 0.02% max. |
UNI EN 1982:2017 - Gun bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>81 | 3.5 | 2.2 | - | - | - | - | - | - | - | 7.5 | - | - | - | - | - | - | - | - | |||
85.5 | 5.8 | 3.5 | 0.5 | 0.01 | 2 | - | 0.25 | 0.03 | 0.01 | 10 | 0.08 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>83 | 4.2 | 4.2 | - | - | - | - | - | - | - | 4.5 | - | - | - | - | - | - | - | - | |||
86.5 | 5.8 | 6 | 0.25 | 0.01 | 2 | - | 0.25 | 0.03 | 0.01 | 6.5 | 0.08 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>85 | 2.7 | 6.2 | - | - | - | - | - | - | - | 1.7 | - | - | - | - | - | - | - | - | |||
88.5 | 3.5 | 8 | 0.2 | 0.01 | 2 | - | 0.25 | 0.03 | 0.01 | 3.2 | 0.08 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>81 | 5.2 | 6.2 | - | - | - | - | - | - | - | 2.3 | - | - | - | - | - | - | - | - | |||
84.5 | 8 | 8 | 0.2 | 0.01 | 2 | - | 0.3 | 0.03 | 0.01 | 5 | 0.08 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>86 | 1.2 | 5.7 | - | - | - | - | - | - | - | 3.2 | - | - | - | - | - | - | - | - | |||
89.5 | 2 | 6.5 | 0.25 | 0.01 | 1 | - | 0.25 | 0.03 | 0.01 | 5 | 0.08 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>84 | 0.2 | 4.2 | - | - | 0.1 | - | - | - | - | 4.5 | - | - | - | - | - | - | - | - | |||
87.5 | 3 | 6 | 0.3 | 0.01 | 0.6 | - | 0.1 | 0.03 | 0.01 | 6.5 | 0.04 | 0.02 | 0.02 | 0.02 | 0.02 | - | - | - | ||||
Notes
2 | Nickel is included in the copper counting |
3 | For drinking water applications, restrictions to the chemical composition of some materials listed in this table may apply according to national regulations/laws |
4 | (Tin +1/2nickel) content shall be in the range 7.0% to 8.0% |
9 | For continuous castings and centrifugal castings, the minimum tin content for ingots shall be 5.4% and for castings 5.2% and the maximum copper content for ingots shall be 85.0% and for castings 86.0% |
UNI EN 1982:2017 - High-lead tin bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>80 | 8.2 | 4.2 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
86.5 | 10 | 6 | 0.2 | 0.01 | 2 | 0.2 | 0.5 | 0.1 | 0.01 | 2 | 0.08 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>78 | 8.2 | 9.2 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
81.5 | 10.5 | 11 | 0.2 | 0.01 | 2 | 0.2 | 0.5 | 0.1 | 0.01 | 2 | 0.08 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>74 | 13.2 | 6.2 | - | - | 0.5 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
79.5 | 17 | 8 | 0.2 | 0.01 | 2 | 0.2 | 0.5 | 0.1 | 0.01 | 2 | 0.08 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>70 | 19 | 4.2 | - | - | 0.5 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
77.5 | 23 | 6 | 0.2 | 0.01 | 2.5 | 0.2 | 0.75 | 0.1 | 0.01 | 2 | 0.08 | - | - | - | - | - | - | - | ||||
Notes
2 | Nickel is included in the copper counting |
UNI EN 1982:2017 - Leaded tin bronze
UNI EN 1982:2017 - Silicon brass
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>78.5 | - | - | - | - | - | - | - | - | 3 | 10 | - | - | - | - | - | - | - | - | |||
82 | 0.6 | 0.25 | 0.5 | 0.1 | 1 | 0.2 | 0.05 | 0.02 | 5 | 20 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>75 | - | - | - | - | - | - | - | 0.02 | 2.7 | 20 | - | - | - | - | - | - | - | - | |||
77 | 0.1 | 0.3 | 0.3 | 0.05 | 0.2 | 0.05 | - | 0.1 | 3.5 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>80 | - | - | - | - | - | 0.03 | - | 0.05 | 2.5 | 1 | - | - | - | - | - | - | - | - | |||
- | 0.1 | 0.3 | 0.3 | 0.3 | 0.1 | 0.09 | - | 0.15 | 4.5 | 7 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>80 | - | - | - | - | - | 0.03 | - | 0.05 | 2.5 | 7 | - | - | - | - | - | - | - | - | |||
- | 0.1 | 0.3 | 0.3 | 0.3 | 0.1 | 0.09 | - | 0.15 | 4.5 | 11 | - | - | - | - | - | - | - | - | ||||
Notes
3 | For drinking water applications, restrictions to the chemical composition of some materials listed in this table may apply according to national regulations/laws |
5 | For grain refinement, boron or zirconium in the µg/g range may be added to the ingot material and castings. This shall be agreed with the customer |
UNI EN 1982:2017 - Special aluminium bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>68 | - | - | 2 | 7 | 1.5 | 8 | - | - | - | - | - | - | - | - | - | - | - | - | |||
77 | 0.05 | 0.5 | 4 | 9 | 4.5 | 15 | - | - | 0.1 | 1 | - | - | - | - | - | 0.05 | - | - | ||||
Notes
14 | Limits are not specified for ingots in this standard. The composition limits for ingots are at the discretion of the purchaser and shall be stated on the inquiry and order |
UNI EN 1982:2017 - Special brass
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>60 | - | - | 1.5 | 4 | - | 3 | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
66 | 0.2 | 0.2 | 3.5 | 7 | 2.7 | 5 | 0.03 | 0.02 | 0.08 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>59 | - | - | 0.5 | 1 | - | 1 | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
67 | 1.5 | 1 | 2 | 2.5 | 2.5 | 3.5 | 0.08 | - | 1 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>55 | - | - | 0.8 | 1.5 | - | 1 | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
65 | 0.2 | 0.3 | 2 | 3 | 2.7 | 3.5 | 0.05 | 0.02 | 0.08 | 40 | - | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>56 | - | - | 0.5 | 0.7 | - | 0.5 | - | - | - | 20 | - | - | - | - | - | - | - | - | |||
64 | 0.5 | 0.8 | 1.8 | 2.2 | 6 | 2.5 | 0.08 | 0.02 | 0.1 | 40 | - | - | - | - | - | - | - | - | ||||
Notes
2 | Nickel is included in the copper counting |
6 | For permanent mould castings the minimum manganese content shall be 0.3% for ingots and castings |
UNI EN 1982:2017 - Tin bronze
Alloy | Cu | Pb | Sn | Fe | Al | Ni | Mn | Sb | P | Si | Zn | S | As | Bi | Cd | Cr | Mg | Co | Se | |||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| //= ($i == 0) ? t("min") : t("max") ?>88.5 | - | 9.3 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
90.5 | 0.8 | 11 | 0.15 | 0.01 | 1.8 | 0.1 | 0.15 | 0.05 | 0.01 | 0.5 | 0.04 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>87 | - | 10.2 | - | - | - | - | - | 0.6 | - | - | - | - | - | - | - | - | - | - | |||
89.3 | 0.25 | 11.5 | 0.1 | 0.01 | 0.1 | 0.05 | 0.05 | 1 | 0.01 | 0.05 | 0.05 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>85.5 | - | 11.2 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
88.5 | 0.6 | 13 | 0.15 | 0.01 | 2 | 0.2 | 0.15 | 0.2 | 0.01 | 0.4 | 0.05 | - | - | - | - | - | - | - | ||||
| //= ($i == 0) ? t("min") : t("max") ?>84 | - | 11.3 | - | - | 1.5 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
87 | 0.2 | 13 | 0.15 | 0.01 | 2.4 | 0.1 | 0.05 | 0.05 | 0.01 | 0.3 | 0.04 | - | - | - | - | - | - | - | ||||
Notes
2 | Nickel is included in the copper counting |
7 | For sand castings for non-bearing applications the phosphorus may be restricted to 0.15% max. |
8 | For continuous castings and centrifugal castings, the minimum tin content for ingots shall be 10.7% and for castings 10.5% and the maximum copper content for ingots and castings shall be 89.0% |